PROSES KARBURASI PADA BAJA KARBON RENDAH DENGAN MENGGUNAKAN KARBON ARANG KAYU BELIAN DAN ARANG KAYU AKASIA

Muh Anhar(1*)

(1) Politeknik Negeri Ketapang
(*) Corresponding Author

Abstract


Low carbon steel has extensive use in the construction field and is grouped into steel which can be processed with machinery (machinery steel). The prominent weakness of this material is the type of failure that often occurs in low carbon steel materials is wear, deformation, chopping, and breaking. The purpose of conducting this research is to find out the process of carburizing on (wood charcoal and acacia wood charcoal) on low carbon steel.This solid carburizing process uses a temperature of 900OC, with a hold time of 30 minutes. The material used is a mixture of wood charcoal with calcium carbonate and acacia wood charcoal with calcium carbonate. Tests carried out were rockwell hardness tests.The test results showed that the hardness of carbon steel which experienced carburizing treatment with acacia wood charcoal = 51.65 HRB. Hardness found in low carbon steel without treatment = 50.3 HRB. Hardness of wood charcoal = 50.6 HRB. Judging from the results above, the low carbon steel without treatment is smaller than carbon steel which is heat treated and carburized.


Keywords


: Heating Process, Solid Carburizing, Hardness, Low Carbon Steel

Article metrics

Abstract views : 30 | views : 4

Full Text:

PDF

References


Djafrie, Sriati. Metalurgi Mekanik, Terjemahan dari Mechanical Metallurgy, Erlangga, Jakarta. 1995.

Dieter, George E. 1993, Metalurgi Mekanik Edisi Ketiga Jilid Pertama. University Of Maryland.

Darmanto, 2006. Pengaruh Holding Time Terhadap Sifat Kekerasan Dengan Refining The Core Pada Proses Carburizing Material Baja Karbon Rendah, UNWAHAS.

Sunardi, Lusiana, R., Fitra, O.A., 2013, Pengaruh Pack Carburizing dan Kekerasan Permukaan Terhadap Umur Fatik Material Poros Baja S45C, Jurnal Foundry Vol.3, pp. 7-12.

Syamsuir, 2003. Pengaruh Karburasi Terhadap Kekerasan Baja DINI5CrNi6 (MS.7210), Thesis,UGM,Yogyakarta.

Iqbal Muhammad ,Pengaruh Temperatur terhadap Sifat Mekanis pada Proses Pengkarbonan Padat Baja Karbon Rendah (Smartek, 2008 - neliti.com)




DOI: https://doi.org/10.35314/ip.v9i2.1001

Refbacks

  • There are currently no refbacks.


Copyright (c) 2019 INOVTEK POLBENG


This Journal has been listed and indexed in :

         

Creative Commons License
inovtek polbeng by http://ejournal.polbeng.ac.id/index.php/IP is licensed under a Creative Commons Attribution-ShareAlike 4.0 International License